The heat treatment of aluminum castings actually belongs to one of the post-treatment processes of casting, which is carried out after the completion of casting and cleaning of aluminum castings. In addition, it will also involve the post-treatment links such as shaping, rough processing, rust prevention treatment, and their actual application is based on the requirements.
The post-treatment of casting is the last process of aluminum casting production, which has a significant impact on the quality of aluminum casting. However, different post-treatment has different effects. In terms of heat treatment, it is used to improve or change the original structure of aluminum casting. The purpose is to eliminate the internal stress of aluminum casting, ensure the casting performance, and prevent the casting from deformation and damage.
Heat treatment of aluminum castings generally includes quenching, annealing, normalizing, as cast tempering, artificial aging, stress relief, softening and graphitization, aiming at different working conditions. For example, casting requires high wear resistance and enough toughness, and its internal structure should be austenite. For this reason, it is necessary to quench the casting, which can be heated to the austenite area to fully austenitize, then quenched and quenched rapidly, so that the austenite can not be transformed and maintained.
The post-treatment of aluminum castings can be divided into three parts: correction, repair and surface finishing. Because some castings will have different degrees of deformation in the process of solidification, cooling and heat treatment, which will make some dimensions out of tolerance, so rectification is needed for repair. The correction is mainly carried out at room temperature or temperature by mechanical force. When the deformation is too large, the casting self weight or external pressure can also be used in the heating furnace for high temperature correction.
The external defects of aluminum castings are mainly repaired by welding, and the rough and uneven surface of castings are generally polished and finished by suspension wheel and high-speed wheel. Rough machining is a post-treatment technology for local aluminum castings. Defects can be found and solved in time after rough machining, and the weight can be reduced, and the scrap and chips can be classified and reused. The antirust treatment is used to avoid the rust of aluminum castings during transportation or storage, and the method of painting primer is used.